مقاله Synthesis and Catalytic Activity of the Mesoporous Silica Nanoparticles in Cumene Hydrocracking Conversion با word
مقاله Synthesis and Catalytic Activity of the Mesoporous Silica Nanoparticles in Cumene Hydrocracking Conversion با word دارای 6 صفحه می باشد و دارای تنظیمات در microsoft word می باشد و آماده پرینت یا چاپ است
فایل ورد مقاله Synthesis and Catalytic Activity of the Mesoporous Silica Nanoparticles in Cumene Hydrocracking Conversion با word کاملا فرمت بندی و تنظیم شده در استاندارد دانشگاه و مراکز دولتی می باشد.
این پروژه توسط مرکز مرکز پروژه های دانشجویی آماده و تنظیم شده است
توجه : در صورت مشاهده بهم ریختگی احتمالی در متون زیر ،دلیل ان کپی کردن این مطالب از داخل فایل ورد می باشد و در فایل اصلی مقاله Synthesis and Catalytic Activity of the Mesoporous Silica Nanoparticles in Cumene Hydrocracking Conversion با word،به هیچ وجه بهم ریختگی وجود ندارد
بخشی از متن مقاله Synthesis and Catalytic Activity of the Mesoporous Silica Nanoparticles in Cumene Hydrocracking Conversion با word :
سال انتشار: 1392
محل انتشار: اولین همایش ملی فناوری های نوین در شیمی و مهندسی شیمی
تعداد صفحات: 6
چکیده:
Mesoporous Silica Nanostructures (MSN) with possess large pore size and volume, high surface area capable to take part in various chemical reactions and have been noticed. These catalysts are able to carry out the cracking conversion of the heavy hydrocarbons, bulky components and polymers to produce the light hydrocarbons or the small organic molecules. Since the pure MSN could not exhibit the catalytic activity due to the low acidity in its framework, introduction of some metals like Al, Zr and Ga to MSN promote its acidity and consequently increase the activity of the catalysts. Incorporation of Al as tetrahedral and octahedral structures generates the acid sites; tetrahedral is responsible of Lewis acid and octahedral is responsible of the Brnsted acid sites. The XRD pattern represented a decreasing in the intense peak for the Al loaded sample in compare to MSN which indicated to reduce in ordered structure. The pyridine-FTIR spectra of HAlMSN catalyst showed the vibrational bands at 1445 and 1545 cm-1 which were related to the Lewis and Brnsted acid sites, respectively. The BET analysis revealed that the surface area was decreased by loading Al and the catalytic activity results showed that the quality of the products was depend on the concentration and distribution of Al content and temperature. The rate of cumene conversion increased with enhancing the amount of Al into the framework and raising the temperature.