مقاله Hydrothermal synthesis of wellدر aligned TiO2 nanorod arrays grown on transparent conducting oxide coated glass با word
مقاله Hydrothermal synthesis of wellدر aligned TiO2 nanorod arrays grown on transparent conducting oxide coated glass با word دارای 3 صفحه می باشد و دارای تنظیمات در microsoft word می باشد و آماده پرینت یا چاپ است
فایل ورد مقاله Hydrothermal synthesis of wellدر aligned TiO2 nanorod arrays grown on transparent conducting oxide coated glass با word کاملا فرمت بندی و تنظیم شده در استاندارد دانشگاه و مراکز دولتی می باشد.
این پروژه توسط مرکز مرکز پروژه های دانشجویی آماده و تنظیم شده است
توجه : در صورت مشاهده بهم ریختگی احتمالی در متون زیر ،دلیل ان کپی کردن این مطالب از داخل فایل ورد می باشد و در فایل اصلی مقاله Hydrothermal synthesis of wellدر aligned TiO2 nanorod arrays grown on transparent conducting oxide coated glass با word،به هیچ وجه بهم ریختگی وجود ندارد
بخشی از متن مقاله Hydrothermal synthesis of wellدر aligned TiO2 nanorod arrays grown on transparent conducting oxide coated glass با word :
سال انتشار: 1393
محل انتشار: پنجمین کنگره بین المللی نانو و فناوری نانو (ICNN2014)
تعداد صفحات: 3
چکیده:
TiO2 is a wide band gap semiconductor that its one dimensional nanostructures have attracted many researchers due to its excellent physical and chemical properties. TiO2 nanorod is used in wide applications such as photocatalysis, photovoltaics, energy storage, electrochromic devices and sensors due to its appropriate electronic band structures, but synthesis of TiO2 nanorod grown perpendicular to the substrate is still a great challenge.in this work, self-assembled and well-aligned TiO2 nanorod arrays are fabricated on pretreated fluorine doped tin oxide coated glass by hydrothermal method at 150C. Energy- dispersive X-ray analyze (EDX), scanning electron microscopy (SEM) are used to characterise TNAs. Oriented TiO2 nanorods are prepared from mixing hydrochlorc acid and acetic acid are well-aligned in compare to TiO2 nanorods arrays are prepared from single acid system. It is found that HOAc can control the morphology and diameter of nanorods. With increasing the value of precursor, the length of nanorod increases but still remains perpendicular to the substrate.